IXEF PARA 1022/9008 索爾維-->PARA-GF50< 阻燃等級: HB 缺口沖擊: 11.22 kJ/m2 符合規定: UL材料特性: 良好的外觀 ? 超高剛性 ? 耐化學性 ? 抗蠕變 ? 通用級 ? 尺寸穩定 ? 良好的消毒性 ? 高流動性 ? 高強度 ? 低吸水率

材料用途: 手機 ? 電器用具 ? 汽車領域的應用 ? 汽車內部零件 ? 電氣元件 ? 家具 ? 高光應用 ? 醫療器械 ? 體育用品應用 ? 外科器械汽車規格: ASTM D6779 PA111G50 ? BOSCH N28 BN05-OX1 Color:0008 Natural ? BOSCH N28 BN05-OX1 Color:9008 Black ? GM GM7001M PAMXD6(A4,A22,A64,BA651,G30,MS1700,NS335)Color:9008 Black ? GM GM7001M PAMXD6(A4,A22,A64,BA751,G30,MS1700,NS350)Color:0008 Natural

注射說明

Hot runners: 250°C to 260°C (482°C to 500°F)StorageIxef? compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef? resins be dried prior to molding following the recommendations found in this datasheet and/or in the Ixef? processing guide.DryingThe material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F).Injection MoldingIxef 1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure.The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F).To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).