LEXAN PC 925A-116阻燃PC---Lexan* 925A Polycarbonate (PC) resin is a non-filled, injection moldable grade of non-chlorinated, non-brominated flame retardant systems that has an UL-94 V0 rating. Lexan 925A is available in transparent and tinted color options and is a general-purpose resin ideal for a wide variety of applications

LEXAN PC 925A-116產品說明：

Lexan*925A聚碳酸酯（PC）樹脂是一種非填充、可注射成型的非氯化、非溴阻燃系統，具有UL-94 V0等級。Lexan 925A有透明和著色兩種顏色可供選擇，是廣泛應用的理想通用樹脂。

LEXAN PC 925A-116

物性信息：

物理性能額定值 (公制)額定值 (英制)測試方法

比重	1.19 g/cc	1.19 g/cc	ASTM D792
線性成型收縮率,Flow	0.0060 - 0.0080 cm/cm @Thickness 3.20 mm	0.0060 - 0.0080 in/in @Thickness 0.126 in	SABIC Method
熔體流動速率	13 g/10 min @Load 1.20 kg, Temperature 300 °C	13 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238

機械性能額定值 (公制)額定值 (英制)測試方法

抗張強度(斷裂)	67.0 MPa	9720 psi	Type I, 50 mm/min; ASTM D638
抗張強度(屈服)	62.0 MPa	8990 psi	Type I, 50 mm/min; ASTM D638
伸長率 (斷裂)	125 %	125 %	Type I, 50 mm/min; ASTM D638
屈服伸長率	6.0 %	6.0 %	Type I, 50 mm/min; ASTM D638
拉伸模量	2.27 GPa	329 ksi	50 mm/min; ASTM D638
彎曲強度	101 MPa	14600 psi	1.3 mm/min, 50 mm span; ASTM D790
彎曲模量	2.37 GPa	344 ksi	1.3 mm/min, 50 mm span; ASTM D790
懸壁梁缺口沖擊強度	8.01 J/cm	15.0 ft-lb/in	ASTM D256
落錘總能量	79.0 J @Temperature 23.0 °C	58.3 ft-lb @Temperature 73.4 °F	ASTM D3763

電氣性能額定值 (公制)額定值 (英制)測試方法

耐電弧性	0.00 - 60 sec	0.00 - 60 sec	Tungsten; ASTM D495
相比耐漏電起痕指數(CTI)	V	V	UL 746A
熱絲引燃 (HWI)	30 - 60 sec	30 - 60 sec	UL 746A
高電弧燃燒，HAI	15 - 30 arcs	15 - 30 arcs	UL 746A
高壓電弧跟蹤率，HVTR	80.0 - 150 mm/min	3.16 - 5.91 in/min	UL 746A