VICTREX? PEEK POLYMER 150XF

Generic Name: 聚醚醚酮(PEEK) - 提供方: Victrex plc

High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, fine powder for compression moulding, easy flow, FDA food contact compliant, colour natural.

 與典型值比較 - Upgrade to compare!

單位: SI 

總覽
材料狀態

已商用：當前有效

搜索 UL 黃卡

Victrex plc

VICTREX? PEEK POLYMER

供貨地區

北美洲

非洲和中東

拉丁美洲

歐洲

亞太地區

機構評級

FDA 食品接觸

外觀

自然色

形式

粉狀

加工方法

壓縮模塑

物理性能

額定值

單位制

測試方法

密度

1.30

g/cm3

ISO 1183表觀密度

0.30

g/cm3

ISO 1183平均顆粒尺寸 - D50

25

μm

ISO 13320-1機械性能

額定值

單位制

測試方法

拉伸模量 (23°C)

4100

MPa

ISO 527-1拉伸應力 (屈服, 23°C)

100

MPa

ISO 527-2拉伸應變 (斷裂, 23°C)

15

%

ISO 527-2彎曲模量 (23°C)

3900

MPa

ISO 178彎曲應力 (23°C)

170

MPa

ISO 178沖擊性能

額定值

單位制

測試方法

懸壁梁缺口沖擊強度 (23°C)

4.5

kJ/m2

ISO 180/A無缺口伊佐德沖擊強度 (23°C)

無斷裂

ISO 180熱性能

額定值

單位制

測試方法

玻璃轉化溫度

ISO 11357-2Onset

143

°C

Midpoint

147

°C

熔融溫度

343

°C

ISO 11357-3充模分析

額定值

單位制

測試方法

熔體粘度 (400°C)

130

Pa·s

ISO 11443補充信息

額定值

單位制

測試方法

Compression Molding Temperature

380 到 400

°C

Drying Time - Compression molding

3.0 到 5.0

hr

干燥溫度 - Compression molding

120 到 150

°C

注射說明

important notes:

1) Processing conditions quoted in our datasheets are typical of those used in our processing laboratories

Data for mould shrinkage should be used for material comparison. Actual mould shrinkage values are highly dependent on part geometry, mould configuration, and processing conditions.

Mould shrinkage differs for along flow and across flow directions. “Along flow” direction is taken as the direction the molten material is travelling when it exits the gate and enters the mould.

Mould shrinkage is expressed as a percent change in dimension of a specimen in relation to mould dimensions.

2) Data are generated in accordance with prevailing national, international and internal standards, and should be used for material comparison. Actual property values are highly dependent on part geometry, mould configuration and processing conditions. Properties may also differ for along flow and across flow directions.

Detailed data available on our website www.victrex.com or upon request.